Optical properties and mineralogical composition of different Saharan mineral dust samples: a laboratory study

C. Linke1, O. Möhler1, A. Veres2, Á. Mohácsi3, Z. Bozóki3, G. Szabó2, and M. Schnaiter1 C. Linke et al.
  • 1Forschungszentrum Karlsruhe, Institute of Meteorology and Climate Research, P.O. Box 3640, 76021 Karlsruhe, Germany
  • 2University of Szeged, Faculty of Natural sciences, Department of Optics and Quantum Electronics, P.O. Box 406, 6701 Szeged, Hungary
  • 3Research Group on Laser Physics of the Hungarian Academy of Sciences, Dóm tér 9., 6720 Szeged, Hungary

Abstract. In aerosol chamber experiments optical properties of resuspended mineral dust samples of defined size distributions were measured. Extinction coefficients (bext) and mass specific extinction cross sections (σext) were determined for Saharan dust samples from different locations. The results for σext were not very sensitive to the type of dust and varied at λ=550 nm between 3.3±0.4 m2 g−1 and 3.7±0.4 m2 g−1. The absorption coefficients (babs) and mass specific absorption cross sections (σabs) were determined with a novel multi-wavelength photo-acoustic absorption spectrometer (PAS). The single scattering albedo was close to 1 (0.98 to 0.99) at 532 nm and 1064 nm, but significantly lower (0.63 to 0.76) at 266 nm. Additionally the chemical and mineralogical composition of the dust samples were analysed with special regard to the iron oxide phases hematite and goethite. At λ=266 nm the mineral dust sample without any detectable iron oxides showed a significantly higher SSA compared to the sample with a hematite content of 0.6 wt-%.